Acid-resistant Coating Material(POLYSHAN H-200)
- Summary
- POLYSHAN H-200 is a 2 pants resin system with silicanoed denatured epoxy resin, which is particularly highly adhesive/flexible. It is a very smooth surface and is widely used as a floor protector for various chemical tanks, glass linings, and various acids and alkali processing sites.
- Chemical Resistance
-
| Division |
Subject |
Hardener |
Combination |
| Exterior |
Transparency |
Emerald Green |
Transparency Emerald Green |
| Compounding ratio (weight) |
100 |
50 |
- |
| Importance(23℃) |
1.75 |
1.14 |
|
| Density(23℃) |
3,300 CPS |
2,700 CPS |
|
| Solids(%) |
100% |
100% |
|
| Housework time(23℃) |
|
|
30minutes |
Enhancement time
Strengthen sustain(23℃)
Fully reinforced |
|
|
4 - 5 hours
3 - 4days |
Coating creation :
FLEXIBLLITY
(MAIN REL BEND) |
|
|
PASS 3.2 m/m |
- Chemical Resistance
-
| Item Name |
Condition |
Item Name |
Condition |
| Tap water |
+ |
nitric acid 10% |
O |
| soft water 10% |
+ |
nitric acid 20% |
- |
| ulfuric acid 98% |
+ |
hydrofluoric acid 10% |
O |
| Hydrochloric acid 36% |
+ |
Chromic acid |
- |
| Formic acid |
+ |
Benzoic acid |
O |
| Gasoline |
+ |
Phthalic Anhydride |
+ |
| Stearic Acid |
+ |
Salicylic Acid |
+ |
| Aniline |
+ |
IPA |
+ |
+ : EXCELLENT O : GOOD - : FAIR(Not accepted)
- Physical Properties
- Compression Strength : 63Kg / ㎡
- Tensile strength : 6.071Kg / ㎟
- Longitude : SHORE D82
- Adhesion Strength : 178 Kg / ㎠
- characteristic
- 100% Property solvent type allows free selection of film thickness.
- It also has excellent workability when applying on a vertical plan and especially when applying to a vertical or floor surface, glass fiber is refilled after sub-treatment as it has high durability or impact oscillation as well as resistance.
- It maintains good adhesion to all substances except non-polar (PE, PP) substances.
- The surface is beautiful and has a good gloss.
- It has excellent wear resistance.
- Various paints can be added to paint in a beautiful color (gray, blue, black).
- Purpose
- Waste water tank lining, tank lining and repair, maintenance and repair of factory floors and walls using acid and alkali, maintenance and repair of acid, alkali PIPE lining and glass lining maintenance and repair
- Work Method
- Remove rust or other dirt from the area to be repaired.
- Wipe the pre-treated portion.
- Mix the subject matter and the hardener exactly with a 100:50 mixing ratio, sufficiently using a spatula and mixing tool.
Here it is better to mix and clean the edges of the container and stir well in left and right directions.
- Mixed products must be used within 30 minutes.
- When lining, the coating thickness shall be at least 2m/m.
For steel structures, it shall be not less than 1 m/m. If “Red wind coat” is done using glass fiber, apply less than 1 m / m in depth and 1 m in depth.
- 4~5 hours after applying it, it does not taint on the hands, but the full hardening is at least 3~4 days later, so it is recommended to use it afterwards.
- Applied area 1㎡ / Kg(2mm standard)
- Packaging unit
- Subject: 2Kg, 6Kg
- Hardener : 1Kg, 3Kg